|Product Name:||High Broad Supply Magnesium Alloy Az31b Az91 We43 Plate / Sheet||Application:||CNC Engraving,Embossing,Etching,Stamping|
|Plate Type:||Hot Roll, Extruded,Cast||Material:||Magnesium Alloy|
|Industrial Plate:||Computer, Printing, Camera, Cellphone||Other Name:||Magnesium Plate/sheet/slab|
High Broad supply magnesium alloy az31b az91 we43 plate / sheet
• Item name: Magnesium slab/plate/sheet
Sheet: Tks: 1 - 6mm; Max. width: 600mm;
Plate: Tks: 6 - 200mm; Max. width: 2500mm;
Max. length: 6000mm
AZ31B Sheet, Plate, Block and coil,slab
1. Product information
a wrought magnesium base alloy with good room-temperature strength and ductility combined with corrosion resistance and weldability. Increased strength is obtained by strain hardening with a subsequent partial anneal (H24 and H26 tempers).
2.Magnesium slab/plate/sheetSize Range:
Sheet: thickness from 1mm to 6mm; Max. width is 600mm; Max. length is 6000mm;
Plate: thickness from 6 mm to 200mm; Max. width is 2500mm; Max. length is 6000mm;
Block: We can supply cut-to-size blocks according to customer's requirements.
Coil: thickness from 0.5 to 2.7mm, max. width 240mm;
3.Magnesium slab/plate/sheet Application :
Sheet and plate in AZ31B find application in medium strength service at temperatures below 150°C. Diverse uses including aerospace, aircraft, concrete tools, 3C (cell phone / camera / computer), speaker cones and textile machinery can all benefit from light weight AZ31B.
AZ31B is non-magnetic and has high electrical and thermal conductivity filling the requirements for RFI and EMI shielding in the electronics and computer industries.
Superplastic forming of AZ31B sheet at elevated temperatures allows production of a wide variety of intricate parts for automotive uses. Monocoque construction utilizing formed sheet can be adapted to many commercial applications.
4.Magnesium slab photo show :
We can surely produce magnesium plate/sheet as per your drawing !
Pls contact us for more details !
ASTM B90/B90M-07; AMS 4375; AMS 4376; AMS 4377
Coefficient of thermal expansion: 26.8 x 10-6K-1
Specific heat: 1040 Jkg-1k-1
Thermal conductivity: 76.9Wm-1k-1
Electrical resistivity: 92nΩm
Modulus of elasticity: 45 x 109Pa;
Poissons ratio: 0.35;
Melting range: 566 - 632°C
Al: 2.5-3.5%; Zn: 0.7-1.3%; Mn: 0.20 – 1.0%; Mg: Balance
No thermal treatment is available for increasing the strength of this alloy after fabrication.
|Alloy and Temper||Thickness (mm)||
0.2% offset (MPa)
In 5.65 √A (%)
|AZ31B-O||0.5 – 1.5||125||221||10|
|1.5 – 6.3||105||221||9|
|6.3 - 75||105||221||8|
|AZ31B-H24||0.5 – 6.3||200||269||5|
|9.5 – 12.7||165||255||8|
|12.7 - 25||152||248||8|
|50 - 80||124||234||7|
|AZ31B-H26||6.3 - 10||186||269||6|
|10 – 12.5||179||262||6|
|12.5 - 20||172||255||5|
|20 – 25||159||255||5|
|25 - 40||152||241||5|
|40 - 50||148||241||5|
The sheet and plate shall conform to the tensile requirements in above Table unless other agreement is made between seller and purchaser. Mechanical Properties for sizes and tempers not shown in above Table shall be as agreed upon by seller and purchaser.
O temper: 67 Rockwell E;
H24 temper: 83 Rockwell E
Excellent weldability with gas shielded arc using AZ61A (preferred) or AZ92A filler rod; post weld stress relief is required to prevent stress corrosion cracking. Resistance welding is excellent.
AZ31B, like all magnesium alloy sheet and plate, machines faster than any other metal. Providing the geometry of the part allows, the limiting factor is the power and speed of the machine rather than the quality of the tool material. The power required per cubic centimeter of metal removed varies from 9 to 14 watts per minute depending on machining operation.
Weight for weight, AZ31B-H24 has proven to be superior to competitive materials in its resistance to denting at moderate energy levels.Dent Resistance of 1mm Gauge Sheet (Dent depth in mm from 25mm spherical redius indentor on 350mm span)
|Impact Energy 0.34 J||Impact Energy 0.62 J||Impact Energy 1.25 J|
6061 – T6
3003 – H14
5052 – H34
2024 – T6
SAE 1010 Mild Steel
All the normal chromating, anodizing, plating, and finishing treatment are readily applicable. AZ31B also responds well to plasma electrolytic oxidation finishing