MMO/Ti Flexible anode / Conductive Polymer linear anode
May 13, 2018
- Conductive Polymer Flexible Anode
|
|
|
| Diameter of flexible anode | 39+/-2 mm |
| Average Thickness of conductive polymer | >= 4 mm |
| Volume Resistivity of conductive polymer | 1.5 Ω˙cm |
| Take a 0.2meter sample and put it into 3% NACI solution with a constant current of 40mA for one month | The consumption of carbon black is of the visible inlet ring radius |
| Output current | 52 mA/m |
| Designed service life of anode | >= 25 years |
| Carbon content of packing coke powder | >= 98% |
| Resistivity of coke powder | <= 0.55 Ω˙cm |
| Fabric Cladding Jacket of anode | Resistant to acid/alkaline and chlorine; Permeable |
| External woven mesh | Resistant to Abrasion and ambient temperature variation |
| Weight of anode | >= 1.3 kgs/meter |
| Length of each coil | 700 meters or customized |
- MMO/Ti Flexible Anode
|
|
|
| Diameter of flexible anode | 39+/-2 mm |
| Diameter of MMO/Ti anode wire | >= 1.0 mm |
| Designed service life of anode | >= 25 years |
| Consumption rate of MMO/Ti anode wire ( with backfill materials) | <= 6 mg/A.a |
| Output current |
|
| Thickness of metallic oxide coating | >= 6 g/m2 |
| Resistivity of mixed metallic oxides(Ω/cm) | 10 -5Ω˙cm |
| Contact Resistance at the joints between andoe and cable | <= 1mΩ |
| Resistance of anode | <= 0.007 Ω/m |
| Carbon content of backfill coke powder | >= 98% |
| Resistivity of coke powder | <= 0.55 Ω˙cm |
| Fabric cladding jacket of anode | Resistant to acid/alkaline and chlorine; Permeable |
| External woven mesh | Resistant to abrasion and ambient temperature variation |
| Weight of anode | >= 1.3 kgs/meter |
| Length of each coil | 700 meters or customized |