MgSc10 Magnesium Scandium Master Alloy Ingot with 10 Percent Scandium for Aerospace Sheet Metal Forming via Vacuum Induction Melting
Product Details:
| Place of Origin: | Hunan, China |
| Brand Name: | HIGH BROAD |
| Certification: | ISO 9001:2015, ISO 14001:2015 |
| Model Number: | MgSc10-INGOT |
Payment & Shipping Terms:
| Minimum Order Quantity: | 100 Kilograms |
|---|---|
| Price: | USD 25-150 / Kilogram |
| Packaging Details: | Vacuum-sealed aluminum foil bag inside export-grade wooden case with desiccant |
| Delivery Time: | 7-15 working days after order confirmation |
| Payment Terms: | T/T,L/C,Western Union,PayPal |
| Supply Ability: | 20000 Kilograms per Month |
|
Detail Information |
|||
| Magnesium Content: | Balance Approx. 90 Wt% | Density: | Approx. 1.85 G/cm3 |
|---|---|---|---|
| Typical Impurities: | Fe <= 0.005%, Si <= 0.01%, O <= 0.03% | Target Sheet YS: | Greater Than 300 MPa T5 |
| Melting Method: | Vacuum Induction Melting Under Argon | Scandium Content: | 10.0 +/- 0.5 Wt% |
| Highlight: | MgSc10 Magnesium Scandium Alloy Ingot,Aerospace Sheet Mg Master Alloy,Scandium 10 Percent Mg Wrought Alloy |
||
Product Description
MgSc10 Magnesium Scandium Master Alloy Ingot 10 Percent Sc for Advanced Aerospace Sheet Metal Forming
This MgSc10-INGOT magnesium scandium rare earth master alloy in ingot form is engineered for advanced magnesium alloy production requiring precise rare earth element additions. Manufactured with high-purity magnesium (99.9% minimum) and premium scandium metal under vacuum induction melting with protective argon atmosphere, it delivers exceptional alloying performance with controlled dissolution characteristics and uniform rare earth distribution.
Product Overview: MgSc10 ingot 10 percent scandium. Aerospace sheet metal. YS above 300 MPa. 500 percent superplastic elongation.
Technical Specifications
| Parameter | Specification |
|---|---|
| Model | MgSc10-INGOT |
| Alloy Type | Magnesium Scandium Rare Earth Master Alloy |
| Scandium Content | 10.0 +/- 0.5 wt% |
| Magnesium Content | Balance approx. 90 wt% |
| Form | Ingot |
| Standard Ingot Weight | 3 kg, 5 kg, 8 kg |
| Melting Method | Vacuum induction melting under argon |
| Typical Impurities | Fe <= 0.005%, Si <= 0.01%, O <= 0.03% |
| Density | Approx. 1.85 g/cm³ |
| Target Sheet YS | Greater than 300 MPa T5 |
Applications
- Aerospace Mg sheet for fuselage skin
- Wing ribs
- Helicopter floors
- Satellite panels
This master alloy provides a cost-effective and reliable method for introducing scandium into magnesium melt compositions with precise compositional control.
Packaging and Delivery
Each ingot is individually vacuum-sealed in aluminum barrier foil bags with desiccant packs. Packaged in export-grade wooden cases with shock-absorbing foam inserts. Standard delivery 7-15 working days after order confirmation. Custom packaging configurations available for large-volume orders.
Want to Know more details about this product